    Производител: BigRep GmbH

    Big Orange

    122,21 лв.
    BigRep True Berlin Color PLA is perfect for everything from prototypes to art projects, end user parts to rapid tooling applications. This filament extrudes very well between 190ºC and 225ºC and has very low moisture absorption.
    *
    *
    Наличност: Please select required attribute(s)

    Features

    PLA (Poly-Lactic Acid) is a thermoplastic aliphatic polyester derived from renewable sources, such as corn, cassava, sugarcane, cereals, or sugar beet. By being derived from biological resources, this type of thermoplastic can be biodegradable under the right conditions. Therefore PLA has a reduced environmental impact compared with other thermoplastics that are derived from fossil fuels.

    PLA can be processed by Extrusion, 3D Printing, Injection Molding, film and sheet casting, providing access to a wide range of products with remarkable properties, which make it suitable for different applications. It is naturally transparent and it can be colored to various degrees of translucency and opacity.

    PLA is an “easy to use” 3D printer filament in comparison to other polymers. It can be printed using low to moderate temperatures and higher speed rates via FFF/FDM. The mechanical behavior, as well as other properties of the final product are widely dependent on the 3D printing conditions, such as extruder temperature, extrusion speed, cooling system, etc. PLA compared to other polymers used for 3D printing demonstrates much less warping and for this reason it’s possible to successfully print without a special cooling system. For applications at higher humidity (above 98%) and higher temperatures (above 60°C) other polymers should be used, such as PRO HT and PETG.

    Filaments should remain sealed when being stored long term in order to prevent absorption of moisture from the air. High moisture content may harm the quality of the extrusion, leading to the clogging of the nozzles, as well as bubbles and spurting.

    Specifications

     

    Filament Net Weight: 2.3 / 4.5 / 8.0 Kg
    Material: Polylactic Acid
    Density: 1.24 g/cm³
    Diameter: 2.85 mm
    Print Temperature Guideline: 205 °C
    Heating Bed: 60 °C
    VST (ISO 306 VST A 120): 60 °C
    Tensile Strength (ISO 527): 60 MPa
    Impact Strength (ISO 179): 7.5 KJ/m²
    Flexural Modulus (ISO 178): 3800 MPa
    Продуктови спецификации
    Filament Material PLA
    Цвят
     
    Nozzle size ≥ 0.15mm
    Print temp ± 180 - 205° C *
    Heat bed ± 0 - 60° C
    Layer height ≥ 0.1mm
    Print speed Medium
    Fan speed 50-100%
    Flow rate ± 100%
    Retraction Yes ± 5 mm
    Experience level Beginner
    Напиши отзив
    • Може да оставите отзив за продукт само след като го закупите.
    • Само регистрирани потребители могат да пишат отзиви
    *
    *
    • Лошо
    • Отлично
    *
    *
    *

    Features

    PLA (Poly-Lactic Acid) is a thermoplastic aliphatic polyester derived from renewable sources, such as corn, cassava, sugarcane, cereals, or sugar beet. By being derived from biological resources, this type of thermoplastic can be biodegradable under the right conditions. Therefore PLA has a reduced environmental impact compared with other thermoplastics that are derived from fossil fuels.

    PLA can be processed by Extrusion, 3D Printing, Injection Molding, film and sheet casting, providing access to a wide range of products with remarkable properties, which make it suitable for different applications. It is naturally transparent and it can be colored to various degrees of translucency and opacity.

    PLA is an “easy to use” 3D printer filament in comparison to other polymers. It can be printed using low to moderate temperatures and higher speed rates via FFF/FDM. The mechanical behavior, as well as other properties of the final product are widely dependent on the 3D printing conditions, such as extruder temperature, extrusion speed, cooling system, etc. PLA compared to other polymers used for 3D printing demonstrates much less warping and for this reason it’s possible to successfully print without a special cooling system. For applications at higher humidity (above 98%) and higher temperatures (above 60°C) other polymers should be used, such as PRO HT and PETG.

    Filaments should remain sealed when being stored long term in order to prevent absorption of moisture from the air. High moisture content may harm the quality of the extrusion, leading to the clogging of the nozzles, as well as bubbles and spurting.

    Specifications

     

    Filament Net Weight: 2.3 / 4.5 / 8.0 Kg
    Material: Polylactic Acid
    Density: 1.24 g/cm³
    Diameter: 2.85 mm
    Print Temperature Guideline: 205 °C
    Heating Bed: 60 °C
    VST (ISO 306 VST A 120): 60 °C
    Tensile Strength (ISO 527): 60 MPa
    Impact Strength (ISO 179): 7.5 KJ/m²
    Flexural Modulus (ISO 178): 3800 MPa
    Продуктови спецификации
    Filament Material PLA
    Цвят
     
    Nozzle size ≥ 0.15mm
    Print temp ± 180 - 205° C *
    Heat bed ± 0 - 60° C
    Layer height ≥ 0.1mm
    Print speed Medium
    Fan speed 50-100%
    Flow rate ± 100%
    Retraction Yes ± 5 mm
    Experience level Beginner