Manufacturer: EnvisionTec

EC 3000

Be the first to review this product

700,00 лв.

Castable • Jewelry EC3000 has been a popular material in EnvisionTEC’s Easy Cast or “EC” material lineup for more than a decade. Our EC materials are known for higher wax content, less thermal expansion during burnout and foolproof casting. With a 55% wax content material, including both liquid and and powder wax, EC3000 is the highest wax material EnvisionTEC offers for printing on its non-continuous DLP printers. Any higher wax content requires printing on cDLM technology with Easy Cast 2.0 C. EC3000 delivers exceptionally crisp detail and a smooth surface finish, along with the clean burnout that delivers foolproof casting with standard investments.

Weight *

Color *

Availability: Please select required attribute(s)

Qty:

Overview
Specifications
Reviews
Contact Us

EnvisionTEC’s innovative direct investment casting material, Easy-Cast EC3000 has three times more wax than any polymer based material, including EnvisionTEC’s EC500 material. It does not boil during burnout, a leading cause of porosity during casting among competitive products. It also reproduces very high crisp detail not achievable by any other wax-like castable product on the market today. EC3000 is the answer you have been waiting for to give you a competitive advantage for investment casting without any porosity or metal flashing in the jewelry and industrial part manufacturing market. EC3000 has negligible ash content on complete burnout which makes it cast as easily as any injection wax pattern.

Key Features

3D prints patterns with crisp details with best-in-class smooth surface finish
High wax content allows for low thermal expansion during burnout
Can be used with most investment powders
Porosity-free castings due to clean, ash-free burnout
Formulated for casting of heavy wall thicknesses in precious and nonprecious metals

Products specifications

Tensile Strength	16.8 MPa
Elongation at Break	7.46 %
Flexural Strength	23 MPa
Flexural Modulus	404 MPa
Bending Strain	10.2%
Izod Impact – Notched	11.03 kJ/m2
Density	1.178 g/cm3
Ignition Temperature	350°C

Write your own review

Product can be reviewed only after purchasing it
Only registered users can write reviews

Review title: *

Review text: *

Rating:

Bad
Excellent

Your name *

Your email *

Enquiry *

Key Features

3D prints patterns with crisp details with best-in-class smooth surface finish
High wax content allows for low thermal expansion during burnout
Can be used with most investment powders
Porosity-free castings due to clean, ash-free burnout
Formulated for casting of heavy wall thicknesses in precious and nonprecious metals

Products specifications

Tensile Strength	16.8 MPa
Elongation at Break	7.46 %
Flexural Strength	23 MPa
Flexural Modulus	404 MPa
Bending Strain	10.2%
Izod Impact – Notched	11.03 kJ/m2
Density	1.178 g/cm3
Ignition Temperature	350°C